Organic silicon dust removal framework

The post-treatment of silicon dust removal skeleton welding is to prevent rust by surface galvanizing. The machine silicon dust removal skeleton is widely used in high temperature and high corrosion environments. Silicon not only has excellent heat resistance, but also excellent performance stability, which provides excellent protection for electrical equipment in wet conditions.

The production process of silicon dust removal skeleton is the same as that of spray dust removal skeleton, except that the temperature and time during the drying process are higher than those of spray dust removal skeleton. The powder sprayed on the surface of the dust removal skeleton is silicon powder, which can have a service life of several decades in natural environment. The dust removal skeleton treated with silicon has excellent heat resistance and low temperature resistance, as well as excellent performance stability, which can extend the service life of the dust removal skeleton.

The production process of silicon dust removal skeleton:

1. Immerse the processed bag cage into the degreasing tank for 15 minutes to remove any oil stains on the surface of the bag cage.

2. Take out the bag cage from the degreasing tank and place it in the cleaning tank for soaking and cleaning, with the aim of removing the degreasing agent from the bag cage.

3. Take out the bag cage from the cleaning tank and place it in the rust removal tank for rust removal treatment, with the aim of enhancing the adsorption force of the metal oxide layer on the dust collector skeleton.

4. Remove the cage bone from the rust removal tank and place it in the phosphating tank for phosphating treatment, with the aim of enhancing the adhesion of the bag cage surface.

5. Place the processed bag cage in the oven at a temperature of $2100 ℃ and dry it for 20-30 minutes to remove moisture from the bag cage and maintain its dryness.

6. Remove the bag cage and evenly spray the prepared silicon onto the surface of the bag cage. The coating thickness is between 60 μ m and 100 μ m.

7. Place the sprayed bag cage in the oven at a temperature of $2220 ℃ and bake for 120 minutes. Afterwards, maintain a temperature of $2200 ℃ and heat set for 30 minutes. The bag cage is naturally cooled to complete the bag cage silicon spraying process.

8. The thickness with strong adhesion of silicon is between 60-70 μ m.

1. Round bag type outer filter bag.

2. Round bag spring type external filter.

3. Flat bag type, external filter type, oval shape, diamond shape.

4. Envelope type

5. Multi section frame, elliptical multi section frame, circular bag type multi section frame, plug-in and chuck type.

6. Finished frames with Venturi tubes, frames packaged in plastic bags or iron frames A neatly arranged diamond frame.